Quantifying Residual Stresses in Resistance Spot Welding of 6061-T6 Aluminum Alloy Sheets via Neutron Diffraction Measurements

Florea, R. S., Hubbard, C. R., Solanki, K. N., Bammann, D., Whittington, W. R., & Marin, E. (2012). Quantifying Residual Stresses in Resistance Spot Welding of 6061-T6 Aluminum Alloy Sheets via Neutron Diffraction Measurements. Journal of Materials Processing Technology. Elsevier. 212, 2358-2370. DOI:10.1016/jmatprotec.2012.06.024.

Residual strains of resistance spot welded joints of 6061-T6 aluminum alloy sheets were measured in three different directions denoted as in-plane longitudinal, in-plane transversal, and normal. The welding process parameters were established to meet or exceed MIL-W-6858D specifications (i.e., approximately 5.7 mm weld nugget and minimum shearing force of 3.8 kN per weld confirmed via quasi-static tensile testing). Electron backscatter diffraction (EBSD) and optical microscopy (OM) were performed to determine grain size and orientation. The residual stress measurements were taken at a series of points along the weld centerline at depths corresponding to the weld mid-plane and at both 1 mm below the top surface of the plate and 1 mm above bottom surface. The residual stresses were captured on the fusion zone (FZ), heat affected zone (HAZ) and base metal (BM) of the resistance spot welded joint. Neutron diffraction results show residual stresses in the weld are approximately 40% lower than yield strength of the parent material. The maximum variation in residual stresses occurs, as expected, in the vertical position of the specimen because of the orientation of electrode clamping forces that produce a non-uniform solidification pattern. Despite the high anisotropy of the welding nugget and surrounding area, a significant result is that measured stress values are negligible in both the horizontal and vertical directions of the specimen. Consequently, microstructure-property relationships characterized here can indeed inform continuum material models for application in multiscale models.